What absorbs at 663 cm⁻¹ in an FTIR spectrum?
Una banda cerca de 663 cm⁻¹ puede apuntar a varios grupos funcionales. A continuación se muestran las asignaciones más probables, clasificadas por cuánta evidencia publicada respalda cada una — cada una trazable a literatura (DOI) y validada de forma cruzada con nuestros más de 130,000 espectros de referencia y grafo de conocimiento.
Backed by 8 cited sources
Respuesta rápida
A band near 663 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Posibles asignaciones de grupos funcionales
| Grupo funcional | Hechos de respaldo | Fuentes citadas | Confianza máxima |
|---|---|---|---|
| Hydroxyl (O-H) | 2 | 2 | 1,0 |
| Silicon-oxygen (Si-O) | 2 | 2 | 1,0 |
| Silicon (Si) | 2 | 2 | 1,0 |
| Carbon bromine | 2 | 2 | 1,0 |
| Secondary amine | 2 | 2 | 1,0 |
| C n single bond | 2 | 2 | 1,0 |
| Amide | 2 | 2 | 1,0 |
| Metal oxygen | 1 | 1 | 1,0 |
| Bromine | 1 | 1 | 1,0 |
| Chlorine | 1 | 1 | 1,0 |
| Siloxane (Si-O-Si) | 1 | 1 | 1,0 |
| Thiol | 1 | 1 | 1,0 |
| Carboxyl (COOH) | 1 | 1 | 0,8 |
La clasificación refleja la evidencia acumulada de la literatura, no una única regla autorizada. Siempre confirme según el contexto de su muestra.
Materiales posibles
| Material | Picos de apoyo | Grupos superpuestos | Fuentes citadas |
|---|---|---|---|
| Silica | 663, 1100, 1080 | Silicon-oxygen (Si-O), Silicon (Si), Hydroxyl (O-H) | 1 |
| copper oxide | 663, 624, 1686 | Hydroxyl (O-H) | 1 |
| hydroxyapatite | 663, 1620, 1639 | Hydroxyl (O-H) | 1 |
Los materiales se muestran solo cuando el mismo grupo de literatura respalda esta banda y al menos un pico característico adicional.
Lógica de espectro
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 663 cm⁻¹ is usually not enough for material identification by itself.
Uso en el mundo real
Este tipo de consulta es común en la identificación de polímeros, cribado de plásticos desconocidos, resolución de problemas de control de calidad, verificación de materiales reciclados y revisión de asignación de picos respaldada por la literatura.
Errores comunes
- Tratar una banda aislada como prueba de un material sin verificar al menos uno o dos picos de apoyo.
- Ignorando superposición: múltiples grupos funcionales pueden contribuir cerca del mismo número de onda.
- Omitir la validación cuando los aditivos, las mezclas, la oxidación o la contaminación puedan distorsionar el espectro.
Consejo de verificación
Cuando persista la ambigüedad, valide la hipótesis con DSC, GC-MS o TGA, especialmente para mezclas, muestras degradadas y polímeros rellenos.
Literatura detrás de estas asignaciones
-
Thiol confianza 1,0
“The second silicate bands are 4 cm-1 in C-S-H broadly characterized as O-Si-O deformation or bending modes, which occur near 451 470cm-1 cm-1 667cm-1 and in C-A-S-H and the band 663 or is due to Si-O-Si bending vibrations.”
He 等 - 2011 - Morphology and Structure of Aluminum Substituted C DOI: 10.4028/www.scientific.net/AMR.287-290.1193 -
confianza 1,0
“Peak at 663 Tensile tests were performed according to ASTM D638 corresponds to the C-Cl stretching in PVC chains.”
Ibrahim 等 - 2011 - A study of poly vinyl chloridepoly(butylene adipa DOI: 10.1007/s10965-010-9486-1 -
Carbon bromine confianza 1,0
“The intense bands situated at about 663 and 1025cm-1 of wavelength were assigned to the stretching vibrational movement of C-Br and”
Jing 等 - 2019 - Biosynthesis of copper oxide nanoparticles and the DOI: 10.1016/j.jphotobiol.2019.111557 -
Amide confianza 1,0
“pneumonia were observed by SEM based on a method reported 663cm-1 C-N C-Br ∼105CFU/mL are due to and stretching vibrational motions.”
Biologically synthesized copper oxide nanoparticles enhanced intracellular damage in ciprofloxacin resistant ESBL producing bacteria DOI: 10.1016/j.micpath.2018.12.017 -
Hydroxyl (O-H) confianza 1,0
“cm-1 Analysis of deuterated samples [50] shows that the relatively sharp peak at 663 is due to the O-H Analysis of deuterated samples [50] shows that the relatively sharp peak at 663 cm-1 is due to the Olibration (see inset in Figure 4).”
Baldassarre 等 - 2020 - Crystal Chemistry and Luminescence Properties of E DOI: 10.3390/cryst10040250 -
confianza 1,0
“The strong bonds between 981.1 cm-1 and 662.7 cm-1 stretching with halogen groups.”
Synthesis and Characterization of Sulfur Nanoparticles of Citrus limon Extract Embedded in Nanohydrogel Formulation: In Vitro and In Vivo Studies DOI: 10.3390/gels9040284 -
confianza 1,0
“is triuoroacetate electrostatic interaction of lanthanum and triarticle cm-1 Si-O-Si La-O-Si 663 assigned to & bond vibrations, chloroacetate with the silica support material, which converts Article.”
Silica supported lanthanum trifluoroacetate and trichloroacetate as an efficient and reusable water compatible Lewis acid catalyst for synthesis of 2,4,5-triarylimidazoles via a solvent-free green approach DOI: 10.1039/d2ra07021a -
Hydroxyl (O-H) confianza 1,0
“Analysis of deuterated samples [56] shows cm-1 that the relatively sharp peak at 663 is due to the O-H libration.”
Paterlini 等 - 2020 - Characterization and Luminescence of Eu3+- and Gd3 DOI: 10.3390/cryst10090806
¿Tiene un espectro con esta banda?
Cargue su espectro FTIR y obtenga un informe de interpretación completo — asignaciones de picos con citas bibliográficas, coincidencias de librerías y una cadena de evidencia con calificación de confianza — en segundos.