Silicon (Si) — Puncak serapan FTIR dan tugasan
Ini ialah nombor gelombang FTIR ciri apabila Silicon (Si) cenderung menyerap, yang dihimpunkan daripada literatur yang diterbitkan dan diperingkat berdasarkan bukti sokongan. Setiap penetapan boleh dijejaki kepada sumber (DOI) dan disahkan silang terhadap 320,000+ spektrum rujukan serta graf pengetahuan kami.
Disokong oleh 8 sumber yang dipetik
Jawapan pantas
Silicon (Si) biasanya ditetapkan dengan mencari kelompok berulang puncak ciri dan bukan satu nombor tepat buku teks. Jadual di bawah menunjukkan di mana literatur paling kerap meletakkan kumpulan ini dalam FTIR, yang disusun mengikut bukti terkumpul.
Puncak FTIR ciri untuk Silicon (Si)
| Nombor gelombang (cm⁻¹) | Fakta sokongan | Sumber dipetik | Keyakinan tertinggi |
|---|---|---|---|
| 800 | 39 | 36 | 1.0 |
| 1000 | 29 | 27 | 1.0 |
| 1100 | 28 | 22 | 1.0 |
| 1080 | 19 | 17 | 1.0 |
| 460 | 19 | 17 | 1.0 |
| 470 | 15 | 14 | 1.0 |
| 950 | 14 | 13 | 1.0 |
| 1050 | 14 | 11 | 1.0 |
| 520 | 13 | 13 | 1.0 |
| 1030 | 13 | 12 | 1.0 |
| 1200 | 12 | 10 | 1.0 |
| 960 | 12 | 9 | 1.0 |
| 450 | 11 | 11 | 1.0 |
| 1090 | 10 | 9 | 1.0 |
| 1020 | 9 | 9 | 1.0 |
| 900 | 9 | 9 | 1.0 |
| 400 | 9 | 8 | 1.0 |
| 1260 | 8 | 8 | 1.0 |
| 970 | 8 | 8 | 1.0 |
| 1037 | 8 | 8 | 1.0 |
| 480 | 8 | 7 | 1.0 |
| 955 | 8 | 7 | 1.0 |
| 940 | 8 | 6 | 1.0 |
| 1035 | 7 | 7 | 1.0 |
| 840 | 7 | 7 | 1.0 |
| 694 | 7 | 7 | 1.0 |
| 938 | 7 | 7 | 1.0 |
| 600 | 7 | 7 | 1.0 |
| 790 | 7 | 7 | 1.0 |
| 795 | 7 | 6 | 1.0 |
Menunjukkan 30 puncak terbaik disokong daripada 715 jumlah untuk Silicon (Si).
Bahan yang mungkin
Logik spektrum
Tugasan kumpulan berfungsi menjadi lebih yakin apabila beberapa jalur yang dijangkakan muncul bersama. Gunakan halaman ini untuk mencari puncak yang paling disokong, kemudian sahkan bahawa sampel yang sama menunjukkan corak yang koheren dan bukannya satu hit terpencil.
Penggunaan dunia sebenar
Halaman-halaman ini berguna untuk analisis bahan yang tidak diketahui, penjelasan puncak dalam laporan, penyelesaian masalah polimer, dan mengesahkan sama ada keluarga bahan calon adalah boleh dipercayai secara kimia.
Kesilapan biasa
- Menggunakan satu halaman kumpulan berfungsi sebagai keputusan bahan lengkap tanpa memeriksa spektrum yang lain.
- Dengan menganggap jalur yang paling kuat sentiasa menjadi yang paling diagnostik.
- Melupakan bahawa pemprosesan, bahan tambahan, penuaan, dan campuran boleh mengalihkan atau melebarkan puncak yang dijangkakan.
Nasihat pengesahan
Gunakan DSC, GC-MS, atau TGA apabila beberapa keluarga bahan berkongsi jalur yang serupa atau apabila kesan campuran menyebabkan tugasan FTIR tidak pasti.
Literatur di sebalik penetapan ini
-
3429 cm⁻¹ keyakinan 1.0
“The FTIR spectra of the cm-1 montmorillonite-carbon nanotube nano filler display bands at 3429, 1076, and 798 which correspond to OH functional groups, Si-O-Si stretching, and Si-O-Si vibration, respectively.”
Synthesis and Physical Properties Characterization of Montmorillonite-modified Carbon Nanotubes Filler DOI: 10.1088/1757-899X/546/4/042004 -
1089 cm⁻¹ keyakinan 1.0
“FTIR spectra showed peaks at 1089 and cm-1, 801 which corresponded to asymmetric and symmetric O-Si-O.”
Fabrication of Biogenic Silica Nanostructures from Sorghum bicolor Leaves for Food Industry Applications DOI: 10.1007/s12633-020-00379-4 -
3604 cm⁻¹ keyakinan 1.0
“3741cm-1 sorption peaks at 3604 and observed on both treatment of H-BEA is as follows: H-BEA powder was imH-BEA and Ca/H-BEA have been assigned to Si (OH) Al mersed in an aqueous solution of an alkaline earth metal nibridge structure and lo”
Phenol oxidation over alkaline earth metal ion exchange beta zeolite in the presence of ketone DOI: 10.1016/j.molcata.2004.08.020 -
1106 cm⁻¹ keyakinan 1.0
“cm(cid:2)1, 1040¨1180 Acknowledgments It shows a weak peak at 1106 which is attributed to the stretching vibration of Si-O.”
Structural characterization of β-SiC nanowires synthesized by direct heating method DOI: 10.1016/j.msec.2005.09.083 -
1000 cm⁻¹ keyakinan 1.0
“In the spectrum peaks are observed cm-1 cm-1 in the region of 1258.88 corresponding to methyl, between 1000 - 1100 a peak cm-1 corresponding to the Si-O-Si bond and a band at 792.10 characteristic of the siloxanes, confirming the presence o”
Fabrication of a silver particle-integrated silicone polymer-covered metal stent against sludge and biofilm formation and stent-induced tissue inflammation DOI: 10.1038/srep35446 -
1009 cm⁻¹ keyakinan 1.0
“3.3 Topographical analysis Si-O-Si modes.20 breathing The spectra display asymmetric cm(cid:1)1, stretching at 1009 which corresponds to the presence of The topographical investigation of pristine the PC, PC/FAC and PC/GFACwerestudiedbyAFM.”
Thin film encapsulation of nano composites of polycarbonate (PC) for thermal management systems DOI: 10.1039/c4ra10183a -
470 cm⁻¹ keyakinan 1.0
“cm-1 The absorption bands centered at around 470, 820, 1170, 2180, and 3300 can be assigned to the Si-N symmetric stretching, Si-N asymmetric stretching, N-H bending, Si-H stretching, and NH stretching modes, respectively.”
Evolution of Optical and Structural Properties of Silicon Nanocrystals Embedded in Silicon Nitride Films with Annealing Temperature DOI: 10.4028/www.scientific.net/JNanoR.49.163 -
721 cm⁻¹ keyakinan 1.0
“381.74 Si-Ob-Si bending vibration 720.8 128.70 725.9 110.96 766.2”
Theoretical and experimental study of structures and properties of cement paste: The nanostructural aspects of C–S–H DOI: 10.1016/j.jpcs.2011.05.001
Lihat Silicon (Si) dalam spektrum anda sendiri
Muat naik spektrum FTIR anda dan dapatkan laporan tafsiran penuh — tugasan puncak dengan petikan literatur, padanan perpustakaan, dan analisis berasaskan literatur — dalam beberapa saat.