Silicon nitrogen — Puncak serapan FTIR dan tugasan
Ini adalah nombor gelombang FTIR ciri di mana Silicon nitrogen cenderung menyerap, disusun dari literatur yang diterbitkan dan disusun berdasarkan bukti sokongan. Setiap tugasan dapat dikesan ke sumber (DOI) dan disahkan silang terhadap 130,000+ spektrum rujukan dan graf pengetahuan kami.
Backed by 8 cited sources
Jawapan pantas
Silicon nitrogen biasanya ditetapkan dengan mencari kelompok berulang puncak ciri dan bukan satu nombor tepat buku teks. Jadual di bawah menunjukkan di mana literatur paling kerap meletakkan kumpulan ini dalam FTIR, yang disusun mengikut bukti terkumpul.
Puncak FTIR ciri untuk Silicon nitrogen
| Nombor gelombang (cm⁻¹) | Fakta sokongan | Sumber dipetik | Keyakinan tertinggi |
|---|---|---|---|
| 850 | 3 | 1 | 1.0 |
| 450 | 2 | 2 | 1.0 |
| 490 | 2 | 1 | 1.0 |
| 904 | 1 | 1 | 1.0 |
| 1162 | 1 | 1 | 1.0 |
| 1300 | 1 | 1 | 1.0 |
| 840 | 1 | 1 | 1.0 |
| 709 | 1 | 1 | 1.0 |
| 1000 | 1 | 1 | 1.0 |
| 849 | 1 | 1 | 1.0 |
| 3335 | 1 | 1 | 1.0 |
| 880 | 1 | 1 | 1.0 |
| 980 | 1 | 1 | 1.0 |
| 923 | 1 | 1 | 1.0 |
| 669 | 1 | 1 | 1.0 |
| 587 | 1 | 1 | 1.0 |
| 964 | 1 | 1 | 1.0 |
| 640 | 1 | 1 | 1.0 |
| 1180 | 1 | 1 | 1.0 |
| 917 | 1 | 1 | 1.0 |
| 700 | 1 | 1 | 1.0 |
| 1040 | 1 | 1 | 1.0 |
| 875 | 1 | 1 | 1.0 |
| 470 | 1 | 1 | 1.0 |
| 1019 | 1 | 1 | 0.9 |
| 1075 | 1 | 1 | 0.7 |
| 1150 | 1 | 1 | 0.6 |
| 1083 | 1 | 0 | 1.0 |
| 1580 | 1 | 0 | 1.0 |
| 3350 | 1 | 0 | 1.0 |
Menunjukkan 30 puncak terbaik disokong daripada 34 jumlah untuk Silicon nitrogen.
Bahan yang mungkin
Logik spektrum
Tugasan kumpulan berfungsi menjadi lebih yakin apabila beberapa jalur yang dijangkakan muncul bersama. Gunakan halaman ini untuk mencari puncak yang paling disokong, kemudian sahkan bahawa sampel yang sama menunjukkan corak yang koheren dan bukannya satu hit terpencil.
Penggunaan dunia sebenar
Halaman-halaman ini berguna untuk analisis bahan yang tidak diketahui, penjelasan puncak dalam laporan, penyelesaian masalah polimer, dan mengesahkan sama ada keluarga bahan calon adalah boleh dipercayai secara kimia.
Kesilapan biasa
- Menggunakan satu halaman kumpulan berfungsi sebagai keputusan bahan lengkap tanpa memeriksa spektrum yang lain.
- Dengan menganggap jalur yang paling kuat sentiasa menjadi yang paling diagnostik.
- Melupakan bahawa pemprosesan, bahan tambahan, penuaan, dan campuran boleh mengalihkan atau melebarkan puncak yang dijangkakan.
Nasihat pengesahan
Gunakan DSC, GC-MS, atau TGA apabila beberapa keluarga bahan berkongsi jalur yang serupa atau apabila kesan campuran menyebabkan tugasan FTIR tidak pasti.
Literatur di sebalik penetapan ini
-
470 cm⁻¹ keyakinan 1.0
“cm-1 The absorption bands centered at around 470, 820, 1170, 2180, and 3300 can be assigned to the Si-N symmetric stretching, Si-N asymmetric stretching, N-H bending, Si-H stretching, and NH stretching modes, respectively.”
Benyahia 等 - 2017 - Evolution of Optical and Structural Properties of DOI: 10.4028/www.scientific.net/JNanoR.49.163 -
490 cm⁻¹ keyakinan 1.0
“(cm(cid:2)2) K Reference Bond Mode Wavenumber (cm(cid:2)1) symmetric stretching 490 - [15] Si-N N-Si3 Si-H Si-H wag-rocking”
Effect of PECVD silicon oxynitride film composition on the surface passivation of silicon wafers DOI: 10.1016/j.solmat.2011.09.052 -
917 cm⁻¹ keyakinan 1.0
“Fourier transform infrared (FTIR) spectroscopy cm-1 analysis showed the Si-N-Si stretching peak at 917 further, the full width at half maxima and Si-N-Si peak position showed their dependency on the deposition temperature.”
Deposition of Silicon Nitride Films using Chemical Vapor deposition for Photovoltaic Applications DOI: 10.1016/j.rinp.2016.11.029 -
450 cm⁻¹ keyakinan 1.0
“LLM confirmed rule peak-group candidate”
Optical and photoelectrochemical properties of nitrogen-doped a-SiC thin films deposited by reactive DOI: 10.1080/2374068X.2021.1890420 -
923 cm⁻¹ keyakinan 1.0
“2.0 10.4 (3) Si-N stretching 923 983 - - sin3 9.2”
Ay 和 Aydinli - 2004 - Comparative investigation of hydrogen bonding in s DOI: 10.1016/j.optmat.2003.12.004 -
880 cm⁻¹ keyakinan 1.0
“The peak at 880 is associated cm-1 with the Si-N stretching mode [25].”
Examination of the Hydrogen Incorporation into Radio Frequency-Sputtered Hydrogenated SiNx Thin Films DOI: 10.3390/coatings11010054 -
849 cm⁻¹ keyakinan 1.0
“cm-1, cm-1, cm-1, 912 and 961 which can be fitted by three symmetric Gaussian bands at 849 represent absorption states of the Si-N stretching mode [52-54].”
Hermann 等 - 2014 - Characterization of semiconductor materials using DOI: 10.1364/OE.22.017948 -
1000 cm⁻¹ keyakinan 1.0
“The absorption bands below 1000 relate to the stretching and deformation vibrations of Si-C, Si-N, C-C, and C-H bonds, which, however are overlapping and consequently cannot be accurately assigned.”
Crosslinking Behavior of UV-Cured Polyorganosilazane as Polymer-Derived Ceramic Precursor in Ambient and Nitrogen Atmosphere DOI: 10.3390/polym13152424
Lihat Silicon nitrogen dalam spektrum anda sendiri
Muat naik spektrum FTIR anda dan dapatkan laporan tafsiran penuh — tugasan puncak dengan petikan literatur, padanan perpustakaan, dan analisis berasaskan literatur — dalam beberapa saat.