Silicon hydride — Puncak serapan FTIR dan tugasan
Ini adalah nombor gelombang FTIR ciri di mana Silicon hydride cenderung menyerap, disusun dari literatur yang diterbitkan dan disusun berdasarkan bukti sokongan. Setiap tugasan dapat dikesan ke sumber (DOI) dan disahkan silang terhadap 130,000+ spektrum rujukan dan graf pengetahuan kami.
Backed by 8 cited sources
Jawapan pantas
Silicon hydride biasanya ditetapkan dengan mencari kelompok berulang puncak ciri dan bukan satu nombor tepat buku teks. Jadual di bawah menunjukkan di mana literatur paling kerap meletakkan kumpulan ini dalam FTIR, yang disusun mengikut bukti terkumpul.
Puncak FTIR ciri untuk Silicon hydride
| Nombor gelombang (cm⁻¹) | Fakta sokongan | Sumber dipetik | Keyakinan tertinggi |
|---|---|---|---|
| 2000 | 11 | 7 | 1.0 |
| 2100 | 10 | 8 | 1.0 |
| 640 | 5 | 3 | 1.0 |
| 2160 | 4 | 3 | 1.0 |
| 2080 | 4 | 3 | 1.0 |
| 2120 | 4 | 3 | 1.0 |
| 630 | 4 | 2 | 1.0 |
| 2169 | 3 | 3 | 1.0 |
| 2159 | 3 | 3 | 1.0 |
| 620 | 3 | 2 | 1.0 |
| 2158 | 3 | 2 | 1.0 |
| 890 | 3 | 2 | 1.0 |
| 2250 | 3 | 2 | 1.0 |
| 885 | 2 | 2 | 1.0 |
| 2200 | 2 | 2 | 1.0 |
| 2109 | 2 | 2 | 1.0 |
| 2170 | 2 | 2 | 1.0 |
| 2110 | 2 | 2 | 1.0 |
| 792 | 2 | 2 | 1.0 |
| 2090 | 2 | 2 | 1.0 |
| 880 | 2 | 2 | 1.0 |
| 2148 | 2 | 2 | 1.0 |
| 2086 | 2 | 2 | 1.0 |
| 2083 | 2 | 2 | 1.0 |
| 910 | 2 | 2 | 0.9 |
| 670 | 2 | 1 | 1.0 |
| 906 | 2 | 1 | 1.0 |
| 2186 | 2 | 1 | 1.0 |
| 907 | 2 | 1 | 1.0 |
| 840 | 2 | 1 | 1.0 |
Menunjukkan 30 puncak terbaik disokong daripada 108 jumlah untuk Silicon hydride.
Logik spektrum
Tugasan kumpulan berfungsi menjadi lebih yakin apabila beberapa jalur yang dijangkakan muncul bersama. Gunakan halaman ini untuk mencari puncak yang paling disokong, kemudian sahkan bahawa sampel yang sama menunjukkan corak yang koheren dan bukannya satu hit terpencil.
Penggunaan dunia sebenar
Halaman-halaman ini berguna untuk analisis bahan yang tidak diketahui, penjelasan puncak dalam laporan, penyelesaian masalah polimer, dan mengesahkan sama ada keluarga bahan calon adalah boleh dipercayai secara kimia.
Kesilapan biasa
- Menggunakan satu halaman kumpulan berfungsi sebagai keputusan bahan lengkap tanpa memeriksa spektrum yang lain.
- Dengan menganggap jalur yang paling kuat sentiasa menjadi yang paling diagnostik.
- Melupakan bahawa pemprosesan, bahan tambahan, penuaan, dan campuran boleh mengalihkan atau melebarkan puncak yang dijangkakan.
Nasihat pengesahan
Gunakan DSC, GC-MS, atau TGA apabila beberapa keluarga bahan berkongsi jalur yang serupa atau apabila kesan campuran menyebabkan tugasan FTIR tidak pasti.
Literatur di sebalik penetapan ini
-
470 cm⁻¹ keyakinan 1.0
“cm-1 The absorption bands centered at around 470, 820, 1170, 2180, and 3300 can be assigned to the Si-N symmetric stretching, Si-N asymmetric stretching, N-H bending, Si-H stretching, and NH stretching modes, respectively.”
Benyahia 等 - 2017 - Evolution of Optical and Structural Properties of DOI: 10.4028/www.scientific.net/JNanoR.49.163 -
2110 cm⁻¹ keyakinan 1.0
“The band at 2110 corresponds to stretching vibrations of Si-H bonds [44,45].”
Mechanical properties, chemical analysis and evaluation of antimicrobial response of Si-DLC coatings fabricated on AISI 316 LVM substrate by a multi-target DC-RF magnetron sputtering method for potential biomedical applications DOI: 10.1016/j.apsusc.2017.03.223 -
3660 cm⁻¹ keyakinan 1.0
“cm-1) cm-1) 3660 and Si-H peak (observed at 2160 417 (1997) relative to Si-O-Si peak as a function of film thickness.”
Bougharouat 等 - 2011 - Plasma polymerization of TEOS for QCM-based VOC va DOI: 10.1051/epjap/2011110144 -
640 cm⁻¹ keyakinan 1.0
“118 Materials Engineering and Mechanical Automation cm-1, C Further, H content ( ) can be calculated according to the absorption intensity at about 640 H * C R which is due to the Si-H wagging mode [9].”
Chen 等 - 2014 - Effect of Deposition Power on the Structure Proper DOI: 10.4028/www.scientific.net/AMM.442.116 -
2940 cm⁻¹ keyakinan 1.0
“The 640 starts to appear stretching modes around 2940 mode.10,11 SC36,13 to Si-H wagging or rocking It gradually diminin and can be clearly seen in SC96 and SC100.”
Chew 等 - 2002 - Hydrogenated amorphous silicon carbide deposition DOI: 10.1063/1.1500418 -
2159 cm⁻¹ keyakinan 1.0
“Figure 14 shows the changes in the silane peak at 2159 The silane peak did not show any intensity for neat asphalt and LPs of CRMA binders interacted at 160-10 or 160-50.”
Effect of used motor oil as a rejuvenator on crumb rubber modifier’s released components to asphalt binder DOI: 10.1177/1477760620918600 -
2300 cm⁻¹ keyakinan 1.0
“IR-spectra of the meso-PS films the absorption between 2300 Let us consider the possible mechanisms of the formation of cm(cid:2)1 and 2000 appears due to Si-H valence vibrations.”
Gorbanyuk 等 - 2006 - Porous silicon microstructure and composition char DOI: 10.1016/j.tsf.2005.08.188 -
490 cm⁻¹ keyakinan 1.0
“(cm(cid:2)2) K Reference Bond Mode Wavenumber (cm(cid:2)1) symmetric stretching 490 - [15] Si-N N-Si3 Si-H Si-H wag-rocking”
Effect of PECVD silicon oxynitride film composition on the surface passivation of silicon wafers DOI: 10.1016/j.solmat.2011.09.052
Lihat Silicon hydride dalam spektrum anda sendiri
Muat naik spektrum FTIR anda dan dapatkan laporan tafsiran penuh — tugasan puncak dengan petikan literatur, padanan perpustakaan, dan analisis berasaskan literatur — dalam beberapa saat.