Methacrylate — FTIR-absorptions-toppe og tildelinger
Dette er de karakteristiske FTIR-bølgetal, hvor Methacrylate har tendens til at absorbere, samlet fra offentliggjort litteratur og rangeret efter understøttende evidens. Hver tildeling kan spores til en kilde (DOI) og er krydsvalideret mod vores 320,000+ referencespektrer og vidensgraf.
Understøttet af 8 citerede kilder
Hurtigt svar
Methacrylate tildeles normalt ved at lede efter en tilbagevendende klynge af karakteristiske toppe frem for et præcist lærebogsnummer. Tabellen nedenfor viser, hvor litteraturen oftest placerer denne gruppe i FTIR, rangeret efter akkumuleret evidens.
Karakteristiske FTIR-toppe for Methacrylate
| Bølgetal (cm⁻¹) | Understøttende fakta | Citerede kilder | Højeste tillid |
|---|---|---|---|
| 1730 | 91 | 88 | 1,0 |
| 1740 | 81 | 74 | 1,0 |
| 1100 | 75 | 70 | 1,0 |
| 1700 | 75 | 69 | 1,0 |
| 1720 | 72 | 67 | 1,0 |
| 1735 | 70 | 66 | 1,0 |
| 1030 | 67 | 60 | 1,0 |
| 1650 | 61 | 59 | 1,0 |
| 1150 | 56 | 55 | 1,0 |
| 1160 | 53 | 52 | 1,0 |
| 1050 | 50 | 47 | 1,0 |
| 1000 | 48 | 48 | 1,0 |
| 1200 | 47 | 46 | 1,0 |
| 1600 | 46 | 44 | 1,0 |
| 1080 | 45 | 43 | 1,0 |
| 1630 | 43 | 41 | 1,0 |
| 1240 | 42 | 41 | 1,0 |
| 1250 | 42 | 39 | 1,0 |
| 1750 | 41 | 39 | 1,0 |
| 1715 | 38 | 36 | 1,0 |
| 1640 | 38 | 35 | 1,0 |
| 1035 | 36 | 32 | 1,0 |
| 1155 | 35 | 35 | 1,0 |
| 1060 | 35 | 34 | 1,0 |
| 1743 | 34 | 34 | 1,0 |
| 1020 | 34 | 32 | 1,0 |
| 1745 | 34 | 32 | 1,0 |
| 1400 | 33 | 32 | 1,0 |
| 1710 | 33 | 27 | 1,0 |
| 1040 | 32 | 30 | 1,0 |
Viser de 30 bedst understøttede toppe ud af 1585 i alt for Methacrylate.
Mulige materialer
Spektrumlogik
En funktionel gruppetildeling bliver mere sikker, når flere forventede bånd optræder sammen. Brug denne side til at finde de bedst understøttede peaks, og bekræft derefter, at den samme prøve udviser et sammenhængende mønster snarere end et enkelt isoleret hit.
Anvendelse i virkeligheden
Disse sider er nyttige til analyse af ukendte materialer, topforklaring i rapporter, polymerfejlfinding og verifikation af, om en kandidatmaterialefamilie er kemisk plausibel.
Almindelige fejl
- Brug af én funktionel-gruppe-side som en komplet materialebedømmelse uden at kontrollere resten af spektret.
- Antager, at det stærkeste bånd altid er det mest diagnostiske.
- At glemme, at forarbejdning, tilsætningsstoffer, ældning og blandinger kan flytte eller udvide forventede toppe.
Verifikationsrådgivning
Brug DSC, GC-MS eller TGA, når flere materialefamilier deler lignende bånd, eller når blandings-effekter gør FTIR-tildelingen usikker.
Litteratur bag disse tildelinger
-
1735 cm⁻¹ tillid 1,0
“The new peak appears cm-1 at 1735 which indicates the presence of a C=O bond from carboxylic acid.”
Synthesis and Physical Properties Characterization of Montmorillonite-modified Carbon Nanotubes Filler DOI: 10.1088/1757-899X/546/4/042004 -
1713 cm⁻¹ tillid 1,0
“This means that the addition shows sharp absorption and low intensity at 1712.8 cm-1 of DVB is able to shift the hydroxyl bonds in blends, which indicates the presence of C=O carbonyl so that DVB makes the blends more compatible.”
Grafting of Oleic Acid On Cyclic Natural Rubber Resiprene-35 Using Dicumyl Peroxide Initiator and Divinylbenzene Compatibilizers For Paint Binder In Polyamide Thermoplastics DOI: 10.13005/ojc/350119 -
853 cm⁻¹ tillid 1,0
“In ATMC the 1289cm-1 ringbreathingmodeisobservedat853cm-1 1351 and corresponds to the C O stretching mode.”
Fourier transform infrared and Raman spectral assignments and analysis of 7-amino-4-trifluoromethylcoumarin DOI: 10.1016/j.saa.2006.09.044 -
1027 cm⁻¹ tillid 1,0
“1137 C-O stretching (ST) 1027 carbohydrate 939”
The Properties of Brown Marine Algae Sargassum turbinarioides and Sargassum ilicifolium Collected From Yogyakarta, Indonesia DOI: 10.14499/indonesianjpharm30iss1pp43 -
1037 cm⁻¹ tillid 1,0
“From FTIR cm(cid:0) 1 C-O-C analysis, observed peaks around 1037 represented the stretching vibrations of the saccharide found in pectin and glycerol.”
Optimization of citron peel pectin and glycerol concentration in the production of edible film using response surface methodology DOI: 10.1016/j.heliyon.2023.e13724 -
2884 cm⁻¹ tillid 1,0
“The characteristic absorption modes observed in the FTIR spectrum at the wavenumbers ~732 , ~842, ~950, ~1048 , ~ 1113, ~ 1244 ,~ 1351,~ 1432, ~ 1468, ~2884 cm-1 6-), and ~2939 are attributed to C-Clst., 𝑠(PF (C-O-C)st., ν(COC) s,w(CH s, δ(”
Arya 等 - 2018 - Effect of variation of different nanofillers on st DOI: 10.1007/s11581-016-1784 -
1114 cm⁻¹ tillid 1,0
“Table 2 shows the shift in C-O-C cm-1 cm-1 band occurring at 1114 towards lower wavenumber side to 1112 on the addition of salt in polymer”
Arya 和 Sharma - 2018 - Structural, microstructural and electrochemical pr DOI: 10.1007/s11581-017-2364-7 -
1723 cm⁻¹ tillid 1,0
“The characteristics sharp peak at 1723 is attributed to stretching vibration of carbonyl (-C=O) group from GMSG/VMSG [46, 47], the intensity of which increases with the increase of GMSG/VMSG contents in the membrane”
Novel Silica Functionalized Monosodium Glutamate/PVA Cross-linked Membranes for Alkali Recovery by Diffusion Dialysis DOI: 10.21203/rs.3.rs-283846/v1
Se Methacrylate i dit eget spektrum
Upload dit FTIR-spektrum og få en fuld fortolkningsrapport — peak-tildelinger med litteraturhenvisninger, biblioteksmatch og en litteraturunderstøttet analyse — på få sekunder.