Anhydride — Puncak serapan FTIR dan tugasan
Ini ialah nombor gelombang FTIR ciri apabila Anhydride cenderung menyerap, yang dihimpunkan daripada literatur yang diterbitkan dan diperingkat berdasarkan bukti sokongan. Setiap penetapan boleh dijejaki kepada sumber (DOI) dan disahkan silang terhadap 320,000+ spektrum rujukan serta graf pengetahuan kami.
Disokong oleh 8 sumber yang dipetik
Jawapan pantas
Anhydride biasanya ditetapkan dengan mencari kelompok berulang puncak ciri dan bukan satu nombor tepat buku teks. Jadual di bawah menunjukkan di mana literatur paling kerap meletakkan kumpulan ini dalam FTIR, yang disusun mengikut bukti terkumpul.
Puncak FTIR ciri untuk Anhydride
| Nombor gelombang (cm⁻¹) | Fakta sokongan | Sumber dipetik | Keyakinan tertinggi |
|---|---|---|---|
| 1780 | 3 | 3 | 1.0 |
| 1784 | 2 | 2 | 1.0 |
| 1770 | 2 | 2 | 1.0 |
| 1850 | 2 | 2 | 1.0 |
| 699 | 1 | 1 | 1.0 |
| 1590 | 1 | 1 | 1.0 |
| 1852 | 1 | 1 | 1.0 |
| 1074 | 1 | 1 | 1.0 |
| 1765 | 1 | 1 | 1.0 |
| 1159 | 1 | 1 | 1.0 |
| 1777 | 1 | 1 | 1.0 |
| 1637 | 1 | 1 | 1.0 |
| 1546 | 1 | 1 | 1.0 |
| 1653 | 1 | 1 | 1.0 |
| 550 | 1 | 1 | 1.0 |
| 1810 | 1 | 1 | 1.0 |
| 1434 | 1 | 1 | 1.0 |
| 1701 | 1 | 1 | 1.0 |
| 1754 | 1 | 1 | 1.0 |
| 1033 | 1 | 1 | 1.0 |
| 730 | 1 | 1 | 1.0 |
| 1761 | 1 | 1 | 1.0 |
| 1791 | 1 | 1 | 1.0 |
| 1280 | 1 | 1 | 1.0 |
| 2363 | 1 | 1 | 1.0 |
| 618 | 1 | 1 | 1.0 |
| 1501 | 1 | 1 | 1.0 |
| 1858 | 1 | 1 | 1.0 |
| 1786 | 1 | 1 | 1.0 |
| 3266 | 1 | 1 | 1.0 |
Menunjukkan 30 puncak terbaik disokong daripada 45 jumlah untuk Anhydride.
Logik spektrum
Tugasan kumpulan berfungsi menjadi lebih yakin apabila beberapa jalur yang dijangkakan muncul bersama. Gunakan halaman ini untuk mencari puncak yang paling disokong, kemudian sahkan bahawa sampel yang sama menunjukkan corak yang koheren dan bukannya satu hit terpencil.
Penggunaan dunia sebenar
Halaman-halaman ini berguna untuk analisis bahan yang tidak diketahui, penjelasan puncak dalam laporan, penyelesaian masalah polimer, dan mengesahkan sama ada keluarga bahan calon adalah boleh dipercayai secara kimia.
Kesilapan biasa
- Menggunakan satu halaman kumpulan berfungsi sebagai keputusan bahan lengkap tanpa memeriksa spektrum yang lain.
- Dengan menganggap jalur yang paling kuat sentiasa menjadi yang paling diagnostik.
- Melupakan bahawa pemprosesan, bahan tambahan, penuaan, dan campuran boleh mengalihkan atau melebarkan puncak yang dijangkakan.
Nasihat pengesahan
Gunakan DSC, GC-MS, atau TGA apabila beberapa keluarga bahan berkongsi jalur yang serupa atau apabila kesan campuran menyebabkan tugasan FTIR tidak pasti.
Literatur di sebalik penetapan ini
-
1710 cm⁻¹ keyakinan 1.0
“and at 1009 However, that of NR/PS-g-MA (with polystyrene, 6/4) peaks of maleic anhydride at 1710 showed only low intensity of the absorption peak.”
Efficiency of maleic anhydride-modified polystyrene/natural rubber blends as sand aggregate binder DOI: 10.1063/5.0015717 -
1002 cm⁻¹ keyakinan 1.0
“cm-1, At 1002 the peak shows CO-O-CO stretching, which indicates the presence of an anhydride group.”
Extraction and Chemical Characterization of Humic Acid from Nitric Acid Treated Lignite and Bituminous Coal Samples DOI: 10.3390/su13168969 -
1220 cm⁻¹ keyakinan 1.0
“The genband at 1220 which is attributed to a five membered eral procedure for esterification of poly(styrene maleic cyclic anhydride (Bellamy, 1975).”
Sugar-linked biodegradable polymers: Regio-specific ester bonds of glucose hydroxyls in their reaction with maleic anhydride functionalized polystyrene and elucidation of the polymer structures formed DOI: 10.1016/j.carbpol.2006.06.035 -
1859 cm⁻¹ keyakinan 1.0
“LLM confirmed rule peak-group candidate”
Spectroscopic Stuides on the Liquid Crystal Alignment Mechanism for Polarized UV-Exposed Organosoluble 6FDA-TFMB Polyimide Films DOI: 10.1080/10587250108028259 -
1780 cm⁻¹ keyakinan 1.0
“Two small peaks at 1780 and 1856cm-' are cyclic anhydride peaks caused by the BTDA, which is present in a slight stoichiometric excess 17 LIQUID CRYSTAL ALIGNMENT A b S 0 r b a n 2014 C e October 1200 1400 1800 1600 1000 28 W ers avenumb 05”
Polarized Infrared Spectroscopic Studies of Polarized UV-exposed Polyimide Films for Liquid Crystal Alignment DOI: 10.1080/10587259808025380 -
618 cm⁻¹ keyakinan 1.0
“The peaks at cm-1 cm-1 618 and 638 due to the stretching vibration of Co-O-Co (or Mn-O-Mn)”
Control of magnetic properties and band gap by Co/Mn ordering and oxygen distributions of La 2 CoMnO 6 DOI: 10.1016/j.jmmm.2017.03.040 -
2363 cm⁻¹ keyakinan 1.0
“The bands that appear in the range 1148-1464 occur as a result of Metal-Oxygen-Metal (M-O-M) such 14 cm-1 as Fe-O-Fe and Co-O-Co [28].The presence of CO is evident by the observation of the band at 2363 15 2”
Effect of heat-treatment on the magnetic and optical properties of Sr0.7Al0.3Fe11.4Mn0.6O19 DOI: 10.1088/2053-1591/aad1e5 -
1280 cm⁻¹ keyakinan 1.0
“of the first peak decreases greatly from 179.0 to 880cm(cid:3)1) peaks (1280, 1080, and are attributed to phosphoric Theresiduesafter theconecalorimeter testwereexaminedfor species.[21] (--O)-O-P) anhydride (P changes in char appearance by”
Synergistic effects of ferric pyrophosphate (FePP) in intumescent flame‐retardant polypropylene DOI: 10.1002/pat.1590
Lihat Anhydride dalam spektrum anda sendiri
Muat naik spektrum FTIR anda dan dapatkan laporan tafsiran penuh — tugasan puncak dengan petikan literatur, padanan perpustakaan, dan analisis berasaskan literatur — dalam beberapa saat.