What absorbs at 1181 cm⁻¹ in an FTIR spectrum?
A band near 1181 cm⁻¹ can point to several functional groups. Below are the most likely assignments, ranked by how much published evidence supports each — every one traceable to literature (DOI) and cross-validated against our 130,000+ reference spectra and knowledge graph.
Backed by 8 cited sources
Câu trả lời nhanh
A band near 1181 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Gán nhóm chức có thể
| Nhóm chức | Sự kiện hỗ trợ | Nguồn tham khảo | Độ tin cậy cao nhất |
|---|---|---|---|
| Methacrylate | 5 | 5 | 1,0 |
| C-O single bond | 5 | 5 | 1,0 |
| Acetate | 5 | 5 | 1,0 |
| Methoxy (OCH3) | 4 | 4 | 1,0 |
| Amide | 2 | 2 | 1,0 |
| Ketone | 1 | 1 | 1,0 |
| Ester | 1 | 1 | 1,0 |
| Carboxyl (COOH) | 1 | 1 | 1,0 |
| Carbonyl (C=O) | 1 | 1 | 1,0 |
| Silicon-oxygen (Si-O) | 1 | 1 | 1,0 |
| Silicon (Si) | 1 | 1 | 1,0 |
| N h | 1 | 1 | 1,0 |
| Hydroxyl (O-H) | 1 | 1 | 1,0 |
| Oxygen heterocycle | 1 | 1 | 1,0 |
| Alkyl C-H | 1 | 1 | 1,0 |
| C c single bond | 1 | 1 | 1,0 |
Xếp hạng phản ánh bằng chứng tài liệu tích lũy, không phải một quy tắc duy nhất có thẩm quyền. Luôn xác nhận với ngữ cảnh mẫu của bạn.
Vật liệu có thể
| Vật liệu | Các đỉnh hỗ trợ | Các nhóm chồng chéo | Nguồn tham khảo |
|---|---|---|---|
| epoxy resin | 1181, 905, 1100 | Methacrylate, Acetate, Methoxy (OCH3) | 1 |
| keratin | 1181, 1635, 1717 | Methacrylate, Acetate | 1 |
| PMMA | 1181, 1722, 1383 | Methacrylate, Acetate, Methoxy (OCH3) | 1 |
Vật liệu chỉ được hiển thị khi cùng một nhóm tài liệu hỗ trợ dải này và ít nhất một đỉnh đặc trưng bổ sung.
Logic phổ
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 1181 cm⁻¹ is usually not enough for material identification by itself.
Sử dụng thực tế
Loại truy vấn này phổ biến trong việc xác định polyme, sàng lọc nhựa chưa xác định, xử lý sự cố QC, xác minh vật liệu tái chế và đánh giá gán đỉnh dựa trên tài liệu.
Các lỗi thường gặp
- Xem xét một dải đơn lẻ như bằng chứng của một vật liệu mà không kiểm tra ít nhất một hoặc hai đỉnh hỗ trợ.
- Bỏ qua chồng lấn: nhiều nhóm chức có thể đóng góp gần cùng một số sóng.
- Bỏ qua xác nhận khi các chất phụ gia, hỗn hợp, quá trình oxy hóa hoặc nhiễm bẩn có thể làm méo phổ.
Lời khuyên xác minh
Khi vẫn còn sự mơ hồ, hãy xác thực giả thuyết bằng DSC, GC-MS hoặc TGA, đặc biệt đối với hỗn hợp, mẫu suy thoái và polyme độn.
Tài liệu tham khảo đằng sau các gán này
-
C c single bond độ tin cậy 1,0
“carbon).37a,b stretching, where the apex denotes a chain bance-frequency spectrum, when the data are collected cm-1 cm-1 A peak at 1181 has contributions from aromatic at a nominal resolution of 4 (see Figure 2 and C-C¢ C-H in-plane bending”
Musto 等 - 2005 - Host-guest interactions and crystalline structure DOI: 10.1021/ma0477899 -
Acetate độ tin cậy 1,0
“Figure 8(b) shows that the peaks observed at 1064 maycorrespondto-C-O-C-,whilepeaksobservedbetween1181.33cm(cid:6)1 binding density that characterizes the number of non-electronic-sharing cm(cid:6)1 C-O interactions between atoms such as io”
Optical characterizations of PMMA/metal oxide nanoparticles thin films: bandgap engineering using a novel derived model DOI: 10.1016/j.heliyon.2021.e05952 -
Oxygen heterocycle độ tin cậy 1,0
“The decrease of the absorption band near 1181 cm-1, which was derived from the bridge between the benzene rings [40], indicates that the backbone chains of epoxy resin can be cut by thermal aging.”
Reinforced Structure Effect on Thermo-Oxidative Stability of Polymer-Matrix Composites: 2-D Plain Woven Composites and 2.5-D Angle-Interlock Woven Composites DOI: 10.3390/polym14173454 -
Hydroxyl (O-H) độ tin cậy 1,0
“0.6 3523cm-1 3000 , O-H deformation vibrastretching vibration at 1441cm-1 1181cm-1 tion at”
Li 和 Yang - 2014 - Fabrication and Characterization of Electrospun Wo DOI: 10.1155/2014/163678 -
độ tin cậy 1,0
“cm-1 2847 cm-1 due to the alkyl groups, a peak at 1648 cm-1 related to the N-H bending belonging to -NH2 2847 due to the alkyl groups, a peak at 1648 related to the N-H bending belonging to -NH 2 cm-1 groups, and peaks at around 1181 and 10”
Acrylic Pressure-Sensitive Adhesive Reinforced with Aluminum Nitride and Its Thermal Properties: Effect of Surface Treatment and Particle Size DOI: 10.3390/coatings10020188 -
Acetate độ tin cậy 1,0
“1181 which is the C-O stretching in -CH-O and micro (< 2 mm) residues.”
Degradation of Film and Rigid Bioplastics During the Thermophilic Phase and the Maturation Phase of Simulated Composting DOI: 10.1007/s10924-021-02098-2 -
Acetate độ tin cậy 1,0
“cm-1 cm-1, cm-1, In addition, the most significant absorptions are observed at 1737 and 1092 1181 cm-1 1274 corresponding to the C=O and C-O-C respectively [12], indicating the existence of ester 1H group.”
Wen 等 - 2018 - A novel oligomer containing DOPO and ferrocene gro DOI: 10.1016/j.polymdegradstab.2018.08.010 -
Acetate độ tin cậy 1,0
“The absorption peak at 1181 was the anti-symmetric stretching of the C-O-C of the ester substance [47].”
Nano Catalysis of Biofuels and Biochemicals from Cotinus coggygria Scop. Wood for Bio-Oil Raw Material DOI: 10.3390/polym14214610
Có phổ với dải này không?
Tải lên phổ FTIR của bạn và nhận báo cáo diễn giải đầy đủ — gán đỉnh với tài liệu tham khảo, kết quả so khớp thư viện và chuỗi bằng chứng xếp hạng độ tin cậy — trong vài giây.