What absorbs at 1181 cm⁻¹ in an FTIR spectrum?
Et bånd nær 1181 cm⁻¹ kan peke på flere funksjonelle grupper. Nedenfor er de mest sannsynlige tildelingene, rangert etter hvor mye publiserte bevis som støtter hver — hver enkelt sporbar til litteratur (DOI) og kryssvalidert mot våre 130 000+ referansespektre og kunnskapsgraf.
Backed by 8 cited sources
Raskt svar
A band near 1181 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Mulige funksjonelle gruppe-tilordninger
| Funksjonell gruppe | Støttende fakta | Siterte kilder | Toppkonfidens |
|---|---|---|---|
| Methacrylate | 5 | 5 | 1.0 |
| C-O single bond | 5 | 5 | 1.0 |
| Acetate | 5 | 5 | 1.0 |
| Methoxy (OCH3) | 4 | 4 | 1.0 |
| Amide | 2 | 2 | 1.0 |
| Ketone | 1 | 1 | 1.0 |
| Ester | 1 | 1 | 1.0 |
| Carboxyl (COOH) | 1 | 1 | 1.0 |
| Carbonyl (C=O) | 1 | 1 | 1.0 |
| Silicon-oxygen (Si-O) | 1 | 1 | 1.0 |
| Silicon (Si) | 1 | 1 | 1.0 |
| N h | 1 | 1 | 1.0 |
| Hydroxyl (O-H) | 1 | 1 | 1.0 |
| Oxygen heterocycle | 1 | 1 | 1.0 |
| Alkyl C-H | 1 | 1 | 1.0 |
| C c single bond | 1 | 1 | 1.0 |
Rangeringen gjenspeiler akkumulert litteraturbevis, ikke en enkelt autoritativ regel. Bekreft alltid mot prøvekonteksten din.
Mulige materialer
| Materiale | Støttetopper | Overlappende grupper | Siterte kilder |
|---|---|---|---|
| epoxy resin | 1181, 905, 1100 | Methacrylate, Acetate, Methoxy (OCH3) | 1 |
| keratin | 1181, 1635, 1717 | Methacrylate, Acetate | 1 |
| PMMA | 1181, 1722, 1383 | Methacrylate, Acetate, Methoxy (OCH3) | 1 |
Materialer vises kun når samme litteraturbase støtter dette båndet og minst en annen karakteristisk topp.
Spektrum-logikk
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 1181 cm⁻¹ is usually not enough for material identification by itself.
Virkelig bruk
Denne typen forespørsel er vanlig i polymeridentifikasjon, screening av ukjent plast, feilsøking i kvalitetskontroll, verifisering av resirkulert materiale og litteraturstøttet gjennomgang av topptilordning.
Vanlige feil
- Behandle ett isolert bånd som bevis på et materiale uten å sjekke minst en eller to støttende topper.
- Ignorerer overlapping: flere funksjonelle grupper kan bidra nær samme bølgetall.
- Hopp over validering når tilsetningsstoffer, blandinger, oksidasjon eller forurensning kan forvrenge spekteret.
Verifiseringsråd
Når tvetydighet gjenstår, valider hypotesen med DSC, GC-MS eller TGA, spesielt for blandinger, nedbrutte prøver og fylte polymerer.
Litteratur bak disse tilordningene
-
C c single bond konfidens 1.0
“carbon).37a,b stretching, where the apex denotes a chain bance-frequency spectrum, when the data are collected cm-1 cm-1 A peak at 1181 has contributions from aromatic at a nominal resolution of 4 (see Figure 2 and C-C¢ C-H in-plane bending”
Musto 等 - 2005 - Host-guest interactions and crystalline structure DOI: 10.1021/ma0477899 -
Acetate konfidens 1.0
“Figure 8(b) shows that the peaks observed at 1064 maycorrespondto-C-O-C-,whilepeaksobservedbetween1181.33cm(cid:6)1 binding density that characterizes the number of non-electronic-sharing cm(cid:6)1 C-O interactions between atoms such as io”
Optical characterizations of PMMA/metal oxide nanoparticles thin films: bandgap engineering using a novel derived model DOI: 10.1016/j.heliyon.2021.e05952 -
Oxygen heterocycle konfidens 1.0
“The decrease of the absorption band near 1181 cm-1, which was derived from the bridge between the benzene rings [40], indicates that the backbone chains of epoxy resin can be cut by thermal aging.”
Reinforced Structure Effect on Thermo-Oxidative Stability of Polymer-Matrix Composites: 2-D Plain Woven Composites and 2.5-D Angle-Interlock Woven Composites DOI: 10.3390/polym14173454 -
Hydroxyl (O-H) konfidens 1.0
“0.6 3523cm-1 3000 , O-H deformation vibrastretching vibration at 1441cm-1 1181cm-1 tion at”
Li 和 Yang - 2014 - Fabrication and Characterization of Electrospun Wo DOI: 10.1155/2014/163678 -
konfidens 1.0
“cm-1 2847 cm-1 due to the alkyl groups, a peak at 1648 cm-1 related to the N-H bending belonging to -NH2 2847 due to the alkyl groups, a peak at 1648 related to the N-H bending belonging to -NH 2 cm-1 groups, and peaks at around 1181 and 10”
Acrylic Pressure-Sensitive Adhesive Reinforced with Aluminum Nitride and Its Thermal Properties: Effect of Surface Treatment and Particle Size DOI: 10.3390/coatings10020188 -
Acetate konfidens 1.0
“1181 which is the C-O stretching in -CH-O and micro (< 2 mm) residues.”
Degradation of Film and Rigid Bioplastics During the Thermophilic Phase and the Maturation Phase of Simulated Composting DOI: 10.1007/s10924-021-02098-2 -
Acetate konfidens 1.0
“cm-1 cm-1, cm-1, In addition, the most significant absorptions are observed at 1737 and 1092 1181 cm-1 1274 corresponding to the C=O and C-O-C respectively [12], indicating the existence of ester 1H group.”
Wen 等 - 2018 - A novel oligomer containing DOPO and ferrocene gro DOI: 10.1016/j.polymdegradstab.2018.08.010 -
Acetate konfidens 1.0
“The absorption peak at 1181 was the anti-symmetric stretching of the C-O-C of the ester substance [47].”
Nano Catalysis of Biofuels and Biochemicals from Cotinus coggygria Scop. Wood for Bio-Oil Raw Material DOI: 10.3390/polym14214610
Har du et spektrum med denne bånden?
Last opp FTIR-spektrumet ditt og få en full tolkningsrapport — topptilordninger med litteraturhenvisninger, bibliotekssøk og en konfidensvurdert beviskjede — på sekunder.