What absorbs at 977 cm⁻¹ in an FTIR spectrum?
A band near 977 cm⁻¹ can point to several functional groups. Below are the most likely assignments, ranked by how much published evidence supports each — every one traceable to literature (DOI) and cross-validated against our 130,000+ reference spectra and knowledge graph.
Backed by 8 cited sources
Răspuns rapid
A band near 977 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Atribuiri posibile ale grupelor funcționale
| Grup funcțional | Fapte suport | Surse citate | Încredere maximă |
|---|---|---|---|
| Silicon-oxygen (Si-O) | 3 | 3 | 1,0 |
| Methoxy (OCH3) | 2 | 2 | 1,0 |
| Methacrylate | 2 | 2 | 1,0 |
| C-O single bond | 2 | 2 | 1,0 |
| Acetate | 2 | 2 | 1,0 |
| Ester | 1 | 1 | 1,0 |
| Siloxane (Si-O-Si) | 1 | 1 | 1,0 |
| Silicon (Si) | 1 | 1 | 1,0 |
| Phosphorus | 1 | 1 | 1,0 |
| Phosphate (PO4) | 1 | 1 | 1,0 |
| Nucleic acid | 1 | 1 | 1,0 |
| Silanol (Si-OH) | 1 | 1 | 1,0 |
| Aromatic ring | 1 | 1 | 0,8 |
| Lipid | 1 | 1 | 0,8 |
Clasamentul reflectă dovezile acumulate din literatură, nu o singură regulă autoritară. Confirmați întotdeauna în contextul mostrei dvs.
Materiale posibile
| Material | Vârfuri suport | Grupuri suprapuse | Surse citate |
|---|---|---|---|
| Silica | 977, 1100, 1080 | Silicon-oxygen (Si-O), Methacrylate | 1 |
| PVDF | 977, 1160, 840 | Methacrylate | 1 |
Materialele sunt afișate numai atunci când același grup de literatură susține această bandă și cel puțin un vârf caracteristic suplimentar.
Logica spectrului
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 977 cm⁻¹ is usually not enough for material identification by itself.
Utilizare în condiții reale
Acest tip de interogare este comun în identificarea polimerilor, screeningul materialelor plastice necunoscute, depanarea QC, verificarea materialelor reciclate și revizuirea atribuirii vârfurilor bazată pe literatură.
Greșeli comune
- Tratarea unei benzi izolate ca dovadă a unui material fără a verifica cel puțin unul sau două vârfuri de susținere.
- Ignorând suprapunerea: mai multe grupuri funcționale pot contribui în apropierea aceluiași număr de undă.
- Omiterea validării atunci când aditivii, amestecurile, oxidarea sau contaminarea pot distorsiona spectrul.
Sfat de verificare
Când ambiguitatea rămâne, validați ipoteza prin DSC, GC-MS sau TGA, în special pentru amestecuri, probe degradate și polimeri umpluți.
Literatura din spatele acestor atribuiri
-
Acetate încredere 1,0
“The GO spectrum presents a broad band at 3192 cm-1, corresponding to the O-H stretching vibration, and peaks associated to the C = O (1734 cm-1), C-OH (1399 cm-1), C-O-C (1207 cm-1) and C-O (977 cm-1) vibrations.”
Joining Caffeic Acid and Hydrothermal Treatment to Produce Environmentally Benign Highly Reduced Graphene Oxide DOI: 10.3390/nano11030732 -
Silanol (Si-OH) încredere 1,0
“The silanol band around 3740 cm-1 and 977 cm-1 decreased in intensity with higher cycle numbers as TMI”
Synthesis of High Surface Area—Group 13—Metal Oxides via Atomic Layer Deposition on Mesoporous Silica DOI: 10.3390/nano12091458 -
Acetate încredere 1,0
“977 978 cm-1 The absorptions in the region between 1200 and 1000 are indicative of C-O-C 417 979 980”
The affiliation of Hexasterias problematica and Halodinium verrucatum sp. nov. to ciliate cysts based on molecular phylogeny and cyst wall composition DOI: 10.1016/j.ejop.2018.09.002 -
încredere 1,0
“Other peaks, ascribed to vibrations from the structure of tobermorite, are at about 1052 cm-1 (νasSi-O-Si), 997 cm-1 (νSi-O-), 977 cm-1”
Phase Composition of Silica Fume—Portland Cement Systems Formed under Hydrothermal Curing Evaluated by FTIR, XRD, and TGA DOI: 10.3390/ma14112786 -
încredere 1,0
“crystalline β phase, where the intensities increase after doping Ag NWs into PVDF, while the intensities cm-1, of the absorption peaks at 977, 796 and 762 which are attributed to the crystalline α phase, drop after doping Ag NWs into PVDF.”
Sensitivity of Pressure Sensors Enhanced by Doping Silver Nanowires DOI: 10.3390/s140609889 -
Nucleic acid încredere 1,0
“The spectrum groups associated with the stretching bands, 43of YAP-KD were associated with positive scores on the phosphodiester bonds from the nucleic acid, and PO 977cm-1 1000cm-1 score plot (PC1) and presented as a negative loading of ph”
Lorthongpanich 等 - 2019 - YAP as a key regulator of adipo-osteogenic differe DOI: 10.1186/s13287-019-1494-4 -
Silicon-oxygen (Si-O) încredere 1,0
“4 4 900, 930 and 977 cm-1 as asymmetric stretching of SiO4 as shown in Table 2.”
Phase Transformation, Optical and Emission Performance of Zinc Silicate Glass-Ceramics Phosphor Derived from the ZnO–B2O3–SLS Glass System DOI: 10.3390/app10144940 -
încredere 1,0
“15, the peak at 977 cm-1 to 1176 was due to asymmetric and symmetric tetrahecm-1 dral of SiO or stretch vibration of Al 2O 3, whereas 977 In conclusion, the compressive strength of silicon manwas due to vibration bending of Si-O-Si [71].”
Effect of Chemical Treatment on Silicon Manganese: Its Morphological, Elemental and Spectral Properties and Its Usage in Concrete DOI: 10.1007/s12633-021-01569-4
Aveți un spectru cu această bandă?
Încărcați spectrul FTIR și obțineți un raport complet de interpretare — atribuiri de peak-uri cu citări din literatură, potriviri cu biblioteca și un lanț de dovezi cu nivel de încredere — în câteva secunde.