What absorbs at 977 cm⁻¹ in an FTIR spectrum?
Una banda cerca de 977 cm⁻¹ puede apuntar a varios grupos funcionales. A continuación se muestran las asignaciones más probables, clasificadas por cuánta evidencia publicada respalda cada una — cada una trazable a literatura (DOI) y validada de forma cruzada con nuestros más de 130,000 espectros de referencia y grafo de conocimiento.
Backed by 8 cited sources
Respuesta rápida
A band near 977 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Posibles asignaciones de grupos funcionales
| Grupo funcional | Hechos de respaldo | Fuentes citadas | Confianza máxima |
|---|---|---|---|
| Silicon-oxygen (Si-O) | 3 | 3 | 1,0 |
| Methoxy (OCH3) | 2 | 2 | 1,0 |
| Methacrylate | 2 | 2 | 1,0 |
| C-O single bond | 2 | 2 | 1,0 |
| Acetate | 2 | 2 | 1,0 |
| Ester | 1 | 1 | 1,0 |
| Siloxane (Si-O-Si) | 1 | 1 | 1,0 |
| Silicon (Si) | 1 | 1 | 1,0 |
| Phosphorus | 1 | 1 | 1,0 |
| Phosphate (PO4) | 1 | 1 | 1,0 |
| Nucleic acid | 1 | 1 | 1,0 |
| Silanol (Si-OH) | 1 | 1 | 1,0 |
| Aromatic ring | 1 | 1 | 0,8 |
| Lipid | 1 | 1 | 0,8 |
La clasificación refleja la evidencia acumulada de la literatura, no una única regla autorizada. Siempre confirme según el contexto de su muestra.
Materiales posibles
| Material | Picos de apoyo | Grupos superpuestos | Fuentes citadas |
|---|---|---|---|
| Silica | 977, 1100, 1080 | Silicon-oxygen (Si-O), Methacrylate | 1 |
| PVDF | 977, 1160, 840 | Methacrylate | 1 |
Los materiales se muestran solo cuando el mismo grupo de literatura respalda esta banda y al menos un pico característico adicional.
Lógica de espectro
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 977 cm⁻¹ is usually not enough for material identification by itself.
Uso en el mundo real
Este tipo de consulta es común en la identificación de polímeros, cribado de plásticos desconocidos, resolución de problemas de control de calidad, verificación de materiales reciclados y revisión de asignación de picos respaldada por la literatura.
Errores comunes
- Tratar una banda aislada como prueba de un material sin verificar al menos uno o dos picos de apoyo.
- Ignorando superposición: múltiples grupos funcionales pueden contribuir cerca del mismo número de onda.
- Omitir la validación cuando los aditivos, las mezclas, la oxidación o la contaminación puedan distorsionar el espectro.
Consejo de verificación
Cuando persista la ambigüedad, valide la hipótesis con DSC, GC-MS o TGA, especialmente para mezclas, muestras degradadas y polímeros rellenos.
Literatura detrás de estas asignaciones
-
Acetate confianza 1,0
“The GO spectrum presents a broad band at 3192 cm-1, corresponding to the O-H stretching vibration, and peaks associated to the C = O (1734 cm-1), C-OH (1399 cm-1), C-O-C (1207 cm-1) and C-O (977 cm-1) vibrations.”
Joining Caffeic Acid and Hydrothermal Treatment to Produce Environmentally Benign Highly Reduced Graphene Oxide DOI: 10.3390/nano11030732 -
Silanol (Si-OH) confianza 1,0
“The silanol band around 3740 cm-1 and 977 cm-1 decreased in intensity with higher cycle numbers as TMI”
Synthesis of High Surface Area—Group 13—Metal Oxides via Atomic Layer Deposition on Mesoporous Silica DOI: 10.3390/nano12091458 -
Acetate confianza 1,0
“977 978 cm-1 The absorptions in the region between 1200 and 1000 are indicative of C-O-C 417 979 980”
The affiliation of Hexasterias problematica and Halodinium verrucatum sp. nov. to ciliate cysts based on molecular phylogeny and cyst wall composition DOI: 10.1016/j.ejop.2018.09.002 -
confianza 1,0
“Other peaks, ascribed to vibrations from the structure of tobermorite, are at about 1052 cm-1 (νasSi-O-Si), 997 cm-1 (νSi-O-), 977 cm-1”
Phase Composition of Silica Fume—Portland Cement Systems Formed under Hydrothermal Curing Evaluated by FTIR, XRD, and TGA DOI: 10.3390/ma14112786 -
confianza 1,0
“crystalline β phase, where the intensities increase after doping Ag NWs into PVDF, while the intensities cm-1, of the absorption peaks at 977, 796 and 762 which are attributed to the crystalline α phase, drop after doping Ag NWs into PVDF.”
Sensitivity of Pressure Sensors Enhanced by Doping Silver Nanowires DOI: 10.3390/s140609889 -
Nucleic acid confianza 1,0
“The spectrum groups associated with the stretching bands, 43of YAP-KD were associated with positive scores on the phosphodiester bonds from the nucleic acid, and PO 977cm-1 1000cm-1 score plot (PC1) and presented as a negative loading of ph”
Lorthongpanich 等 - 2019 - YAP as a key regulator of adipo-osteogenic differe DOI: 10.1186/s13287-019-1494-4 -
Silicon-oxygen (Si-O) confianza 1,0
“4 4 900, 930 and 977 cm-1 as asymmetric stretching of SiO4 as shown in Table 2.”
Phase Transformation, Optical and Emission Performance of Zinc Silicate Glass-Ceramics Phosphor Derived from the ZnO–B2O3–SLS Glass System DOI: 10.3390/app10144940 -
confianza 1,0
“15, the peak at 977 cm-1 to 1176 was due to asymmetric and symmetric tetrahecm-1 dral of SiO or stretch vibration of Al 2O 3, whereas 977 In conclusion, the compressive strength of silicon manwas due to vibration bending of Si-O-Si [71].”
Effect of Chemical Treatment on Silicon Manganese: Its Morphological, Elemental and Spectral Properties and Its Usage in Concrete DOI: 10.1007/s12633-021-01569-4
¿Tiene un espectro con esta banda?
Cargue su espectro FTIR y obtenga un informe de interpretación completo — asignaciones de picos con citas bibliográficas, coincidencias de librerías y una cadena de evidencia con calificación de confianza — en segundos.