What absorbs at 663 cm⁻¹ in an FTIR spectrum?
A band near 663 cm⁻¹ can point to several functional groups. Below are the most likely assignments, ranked by how much published evidence supports each — every one traceable to literature (DOI) and cross-validated against our 130,000+ reference spectra and knowledge graph.
Backed by 8 cited sources
إجابة سريعة
A band near 663 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
تعيينات المجموعات الوظيفية المحتملة
| مجموعة وظيفية | حقائق داعمة | المصادر المستشهد بها | أعلى ثقة |
|---|---|---|---|
| Hydroxyl (O-H) | 2 | 2 | 1,0 |
| Silicon-oxygen (Si-O) | 2 | 2 | 1,0 |
| Silicon (Si) | 2 | 2 | 1,0 |
| Carbon bromine | 2 | 2 | 1,0 |
| Secondary amine | 2 | 2 | 1,0 |
| C n single bond | 2 | 2 | 1,0 |
| Amide | 2 | 2 | 1,0 |
| Metal oxygen | 1 | 1 | 1,0 |
| Bromine | 1 | 1 | 1,0 |
| Chlorine | 1 | 1 | 1,0 |
| Siloxane (Si-O-Si) | 1 | 1 | 1,0 |
| Thiol | 1 | 1 | 1,0 |
| Carboxyl (COOH) | 1 | 1 | 0,8 |
يعكس الترتيب الأدلة الأدبية المتراكمة، وليس قاعدة واحدة موثوقة. تأكد دائمًا من سياق عينتك.
المواد المحتملة
| مادة | القمم الداعمة | المجموعات المتداخلة | المصادر المستشهد بها |
|---|---|---|---|
| Silica | 663, 1100, 1080 | Silicon-oxygen (Si-O), Silicon (Si), Hydroxyl (O-H) | 1 |
| copper oxide | 663, 624, 1686 | Hydroxyl (O-H) | 1 |
| hydroxyapatite | 663, 1620, 1639 | Hydroxyl (O-H) | 1 |
تظهر المواد فقط عندما يدعم نفس مجموعة الأدبيات هذا النطاق وذروة مميزة إضافية واحدة على الأقل.
منطق الطيف
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 663 cm⁻¹ is usually not enough for material identification by itself.
الاستخدام في العالم الحقيقي
هذا النوع من الاستعلام شائع في تحديد البوليمر، وفحص البلاستيك غير المعروف، واستكشاف أخطاء مراقبة الجودة، والتحقق من المواد المعاد تدويرها، ومراجعة تعيين القمم المدعومة بالأدبيات.
الأخطاء الشائعة
- معالجة نطاق معزول واحد كدليل على المادة دون التحقق من ذروة داعمة واحدة أو اثنتين على الأقل.
- تجاهل التداخل: يمكن أن تساهم مجموعات وظيفية متعددة بالقرب من نفس رقم الموجة.
- تخطي التحقق من الصحة عندما قد تؤدي الإضافات أو الخلائط أو الأكسدة أو التلوث إلى تشويه الطيف.
نصيحة التحقق
عندما يبقى الغموض، تحقق من الفرضية باستخدام DSC أو GC-MS أو TGA، خاصة للمخاليط والعينات المتحللة والبوليمرات المملوءة.
الأدبيات وراء هذه التعيينات
-
Thiol الثقة 1,0
“The second silicate bands are 4 cm-1 in C-S-H broadly characterized as O-Si-O deformation or bending modes, which occur near 451 470cm-1 cm-1 667cm-1 and in C-A-S-H and the band 663 or is due to Si-O-Si bending vibrations.”
He 等 - 2011 - Morphology and Structure of Aluminum Substituted C DOI: 10.4028/www.scientific.net/AMR.287-290.1193 -
الثقة 1,0
“Peak at 663 Tensile tests were performed according to ASTM D638 corresponds to the C-Cl stretching in PVC chains.”
Ibrahim 等 - 2011 - A study of poly vinyl chloridepoly(butylene adipa DOI: 10.1007/s10965-010-9486-1 -
Carbon bromine الثقة 1,0
“The intense bands situated at about 663 and 1025cm-1 of wavelength were assigned to the stretching vibrational movement of C-Br and”
Jing 等 - 2019 - Biosynthesis of copper oxide nanoparticles and the DOI: 10.1016/j.jphotobiol.2019.111557 -
Amide الثقة 1,0
“pneumonia were observed by SEM based on a method reported 663cm-1 C-N C-Br ∼105CFU/mL are due to and stretching vibrational motions.”
Biologically synthesized copper oxide nanoparticles enhanced intracellular damage in ciprofloxacin resistant ESBL producing bacteria DOI: 10.1016/j.micpath.2018.12.017 -
Hydroxyl (O-H) الثقة 1,0
“cm-1 Analysis of deuterated samples [50] shows that the relatively sharp peak at 663 is due to the O-H Analysis of deuterated samples [50] shows that the relatively sharp peak at 663 cm-1 is due to the Olibration (see inset in Figure 4).”
Baldassarre 等 - 2020 - Crystal Chemistry and Luminescence Properties of E DOI: 10.3390/cryst10040250 -
الثقة 1,0
“The strong bonds between 981.1 cm-1 and 662.7 cm-1 stretching with halogen groups.”
Synthesis and Characterization of Sulfur Nanoparticles of Citrus limon Extract Embedded in Nanohydrogel Formulation: In Vitro and In Vivo Studies DOI: 10.3390/gels9040284 -
الثقة 1,0
“is triuoroacetate electrostatic interaction of lanthanum and triarticle cm-1 Si-O-Si La-O-Si 663 assigned to & bond vibrations, chloroacetate with the silica support material, which converts Article.”
Silica supported lanthanum trifluoroacetate and trichloroacetate as an efficient and reusable water compatible Lewis acid catalyst for synthesis of 2,4,5-triarylimidazoles via a solvent-free green approach DOI: 10.1039/d2ra07021a -
Hydroxyl (O-H) الثقة 1,0
“Analysis of deuterated samples [56] shows cm-1 that the relatively sharp peak at 663 is due to the O-H libration.”
Paterlini 等 - 2020 - Characterization and Luminescence of Eu3+- and Gd3 DOI: 10.3390/cryst10090806
هل لديك طيف بهذه الحزمة؟
قم بتحميل طيف FTIR الخاص بك واحصل على تقرير تفسير كامل — تعيينات الذروة مع استشهادات الأدبيات، مطابقات المكتبة، وسلسلة أدلة مصنفة الثقة — في ثوانٍ.