What absorbs at 2364 cm⁻¹ in an FTIR spectrum?
A band near 2364 cm⁻¹ can point to several functional groups. Below are the most likely assignments, ranked by how much published evidence supports each — every one traceable to literature (DOI) and cross-validated against our 130,000+ reference spectra and knowledge graph.
Backed by 6 cited sources
Risposta rapida
A band near 2364 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Possibili assegnazioni di gruppi funzionali
| Gruppo funzionale | Fatti di supporto | Fonti citate | Affidabilità massima |
|---|---|---|---|
| Borate | 1 | 1 | 1,0 |
| Carbon dioxide | 1 | 1 | 1,0 |
| Hydroxyl (O-H) | 1 | 1 | 1,0 |
| Water (H2O) | 1 | 1 | 1,0 |
| Aromatic ring | 1 | 1 | 1,0 |
| Methoxy (OCH3) | 1 | 1 | 1,0 |
| Methacrylate | 1 | 1 | 1,0 |
| C-O single bond | 1 | 1 | 1,0 |
| Acetate | 1 | 1 | 1,0 |
| Secondary amine | 1 | 0 | 1,0 |
| N h | 1 | 0 | 1,0 |
La classifica riflette le prove bibliografiche accumulate, non una singola regola autorevole. Conferma sempre nel contesto del tuo campione.
Logica dello spettro
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 2364 cm⁻¹ is usually not enough for material identification by itself.
Utilizzo nel mondo reale
Questo tipo di richiesta è comune nell＇identificazione dei polimeri, nello screening di plastiche sconosciute, nella risoluzione dei problemi di controllo qualità, nella verifica dei materiali riciclati e nella revisione dell＇assegnazione dei picchi supportata dalla letteratura.
Errori comuni
- Trattare una banda isolata come prova di un materiale senza verificare almeno uno o due picchi di supporto.
- Ignorando la sovrapposizione: più gruppi funzionali possono contribuire vicino allo stesso numero d＇onda.
- Saltare la convalida quando additivi, miscele, ossidazione o contaminazione possono distorcere lo spettro.
Consiglio di verifica
Quando permangono ambiguità, convalida l＇ipotesi con DSC, GC-MS o TGA, specialmente per miscele, campioni degradati e polimeri caricati.
Letteratura dietro queste assegnazioni
-
Acetate affidabilità 1,0
“7c, partial decomposition of C-O bands at 2364 preparing the oxide materials, and are associated with metal oxide and cm-1 may describe the bonds in the octahedra sites [44,51].”
Low-temperature synthesis of Sr2FeMoO6 double perovskite; structure, morphology, and magnetic properties DOI: 10.1016/j.ceramint.2020.03.264 -
Aromatic ring affidabilità 1,0
“The weak bands at 2364 and of aromatic ring comand sharp strong peak at pound.”
Olajire 和 Mohammed - 2020 - Green synthesis of nickel oxide nanoparticles and DOI: 10.1016/j.apt.2019.10.012 -
Water (H2O) affidabilità 1,0
“Also, SeH weak bands associated with vibrations are also seen in the glass cm-1and~2332 cm-1.Inaddition,thebandabout samples at~2364 cm-1 ~1640 is observed which is related to the presence of water absorbed from air whilepelletizing samples”
Sharma 等 - 2017 - Impact of CuS on the crystallization kinetics of N DOI: 10.1016/j.jnoncrysol.2017.09.046 -
Hydroxyl (O-H) affidabilità 1,0
“band at 871 and broad band at 1414 This characteristic doublet recorded between cm-1 2334 and 2364 can be assigned to the stretching vibration of OH groups, and explained B.”
Colovic 等 - 2013 - Creating of Highly Active Calcium-Silicate Phases DOI: 10.2298/SOS1303341C -
Carbon dioxide affidabilità 1,0
“cm(cid:3)1 cm(cid:3)1) 2390-2250 tion bands in the (maxima at 2364 and 730-590cm(cid:3)1(maxima at669cm(cid:3)1) regionswere characteristic on bands of CO 2.”
Surface hardness and flammability of Na2SiO3 and nano-TiO2 reinforced wood composites DOI: 10.1039/c9ra05200c -
Borate affidabilità 1,0
“2371.2cm-1, trigonal The peaks at 2364.5 to are due to B-O symmetric stretching vibration in BO units from Pyro 3 bands15.”
Takai 等 - 2019 - Gamma Ray and FTIR Studies in Zinc Doped Lead Bora DOI: 10.1590/1980-5373-MR-2018-0404