Dette er de karakteristiske FTIR-bølgetal, hvor Siloxane (Si-O-Si) har tendens til at absorbere, samlet fra offentliggjort litteratur og rangeret efter understøttende evidens. Hver tildeling kan spores til en kilde (DOI) og er krydsvalideret mod vores 320,000+ referencespektrer og vidensgraf.
Understøttet af 8 citerede kilder
Hurtigt svar
Siloxane (Si-O-Si) tildeles normalt ved at lede efter en tilbagevendende klynge af karakteristiske toppe frem for et præcist lærebogsnummer. Tabellen nedenfor viser, hvor litteraturen oftest placerer denne gruppe i FTIR, rangeret efter akkumuleret evidens.
Karakteristiske FTIR-toppe for Siloxane (Si-O-Si)
| Bølgetal (cm⁻¹) | Understøttende fakta | Citerede kilder | Højeste tillid |
|---|---|---|---|
| 800 | 37 | 35 | 1,0 |
| 1100 | 24 | 21 | 1,0 |
| 460 | 21 | 19 | 1,0 |
| 1000 | 18 | 16 | 1,0 |
| 1080 | 17 | 14 | 1,0 |
| 1030 | 14 | 14 | 1,0 |
| 470 | 13 | 11 | 1,0 |
| 1090 | 12 | 11 | 1,0 |
| 1070 | 10 | 9 | 1,0 |
| 1200 | 10 | 9 | 1,0 |
| 1020 | 9 | 9 | 1,0 |
| 1060 | 9 | 8 | 1,0 |
| 1097 | 9 | 8 | 1,0 |
| 1050 | 9 | 7 | 1,0 |
| 795 | 8 | 8 | 1,0 |
| 1035 | 7 | 7 | 1,0 |
| 798 | 7 | 7 | 1,0 |
| 467 | 7 | 7 | 1,0 |
| 796 | 6 | 6 | 1,0 |
| 1099 | 6 | 6 | 1,0 |
| 450 | 6 | 6 | 1,0 |
| 500 | 6 | 6 | 1,0 |
| 1010 | 6 | 5 | 1,0 |
| 810 | 6 | 4 | 1,0 |
| 1096 | 5 | 5 | 1,0 |
| 1083 | 5 | 5 | 1,0 |
| 482 | 5 | 5 | 1,0 |
| 790 | 5 | 5 | 1,0 |
| 1088 | 5 | 5 | 1,0 |
| 1075 | 5 | 5 | 1,0 |
Viser de 30 bedst understøttede toppe ud af 448 i alt for Siloxane (Si-O-Si).
Mulige materialer
Spektrumlogik
En funktionel gruppetildeling bliver mere sikker, når flere forventede bånd optræder sammen. Brug denne side til at finde de bedst understøttede peaks, og bekræft derefter, at den samme prøve udviser et sammenhængende mønster snarere end et enkelt isoleret hit.
Anvendelse i virkeligheden
Disse sider er nyttige til analyse af ukendte materialer, topforklaring i rapporter, polymerfejlfinding og verifikation af, om en kandidatmaterialefamilie er kemisk plausibel.
Almindelige fejl
- Brug af én funktionel-gruppe-side som en komplet materialebedømmelse uden at kontrollere resten af spektret.
- Antager, at det stærkeste bånd altid er det mest diagnostiske.
- At glemme, at forarbejdning, tilsætningsstoffer, ældning og blandinger kan flytte eller udvide forventede toppe.
Verifikationsrådgivning
Brug DSC, GC-MS eller TGA, når flere materialefamilier deler lignende bånd, eller når blandings-effekter gør FTIR-tildelingen usikker.
Litteratur bag disse tildelinger
-
3429 cm⁻¹ tillid 1,0
“The FTIR spectra of the cm-1 montmorillonite-carbon nanotube nano filler display bands at 3429, 1076, and 798 which correspond to OH functional groups, Si-O-Si stretching, and Si-O-Si vibration, respectively.”
Synthesis and Physical Properties Characterization of Montmorillonite-modified Carbon Nanotubes Filler DOI: 10.1088/1757-899X/546/4/042004 -
801 cm⁻¹ tillid 1,0
“In addition, BSNs showed a band at cm-1, 801 About 50,000 human colon cancer cells were seeded in each which was assigned to the symmetric stretching Si-O-Si vibration of [29].”
Fabrication of Biogenic Silica Nanostructures from Sorghum bicolor Leaves for Food Industry Applications DOI: 10.1007/s12633-020-00379-4 -
984 cm⁻¹ tillid 1,0
“The absorption peaks at 984 cm(cid:1)1 are due to siloxane functionality.”
Synthesis of UV‐curable difunctional silane monomer based on 3‐methacryloxy propyl trimethoxysilane (3‐MPTS) and its UV‐curing characteristics and thermal stability DOI: 10.1002/app.31266 -
1000 cm⁻¹ tillid 1,0
“In the spectrum peaks are observed cm-1 cm-1 in the region of 1258.88 corresponding to methyl, between 1000 - 1100 a peak cm-1 corresponding to the Si-O-Si bond and a band at 792.10 characteristic of the siloxanes, confirming the presence o”
Fabrication of a silver particle-integrated silicone polymer-covered metal stent against sludge and biofilm formation and stent-induced tissue inflammation DOI: 10.1038/srep35446 -
1009 cm⁻¹ tillid 1,0
“3.3 Topographical analysis Si-O-Si modes.20 breathing The spectra display asymmetric cm(cid:1)1, stretching at 1009 which corresponds to the presence of The topographical investigation of pristine the PC, PC/FAC and PC/GFACwerestudiedbyAFM.”
Thin film encapsulation of nano composites of polycarbonate (PC) for thermal management systems DOI: 10.1039/c4ra10183a -
4000 cm⁻¹ tillid 1,0
“The FT-IR data was revealed the existence of peaks at 4000 400 showing the siloxane & silanol groups were present, Fluorescence Spectrophotometer, SEM and EDS.”
Banoth 等 - 2022 - Sustainable Thermochemical Extraction of Amorphous DOI: 10.21203/rs.3.rs-657645/v1 -
623 cm⁻¹ tillid 1,0
“cm(cid:3)1 The vibrational signature at 623 corresponds 2087 Anode reaction to Si-O-Si stretching with full width at half maxima (fwhm) of cm(cid:3)1.”
Synthesis and Characterization of Silicon Nanowires by Electroless Etching DOI: 10.1007/s11665-018-3179-z -
1049 cm⁻¹ tillid 1,0
“The results indicate a strong affinity cm-1 metric stretching around 1049 and Si-O-Si bendof ppTEOS film for methanol gas.”
Bougharouat 等 - 2011 - Plasma polymerization of TEOS for QCM-based VOC va DOI: 10.1051/epjap/2011110144
Se Siloxane (Si-O-Si) i dit eget spektrum
Upload dit FTIR-spektrum og få en fuld fortolkningsrapport — peak-tildelinger med litteraturhenvisninger, biblioteksmatch og en litteraturunderstøttet analyse — på få sekunder.