N-O bond — Puncak serapan FTIR dan tugasan
Ini adalah nombor gelombang FTIR ciri di mana N-O bond cenderung menyerap, disusun dari literatur yang diterbitkan dan disusun berdasarkan bukti sokongan. Setiap tugasan dapat dikesan ke sumber (DOI) dan disahkan silang terhadap 130,000+ spektrum rujukan dan graf pengetahuan kami.
Backed by 8 cited sources
Jawapan pantas
N-O bond biasanya ditetapkan dengan mencari kelompok berulang puncak ciri dan bukan satu nombor tepat buku teks. Jadual di bawah menunjukkan di mana literatur paling kerap meletakkan kumpulan ini dalam FTIR, yang disusun mengikut bukti terkumpul.
Puncak FTIR ciri untuk N-O bond
| Nombor gelombang (cm⁻¹) | Fakta sokongan | Sumber dipetik | Keyakinan tertinggi |
|---|---|---|---|
| 1384 | 12 | 11 | 1.0 |
| 1700 | 8 | 8 | 1.0 |
| 1500 | 8 | 7 | 1.0 |
| 400 | 7 | 7 | 1.0 |
| 1530 | 7 | 4 | 1.0 |
| 1600 | 6 | 6 | 1.0 |
| 1350 | 6 | 5 | 1.0 |
| 3300 | 5 | 5 | 1.0 |
| 3000 | 5 | 3 | 1.0 |
| 1540 | 4 | 4 | 1.0 |
| 3500 | 4 | 4 | 1.0 |
| 2200 | 4 | 4 | 1.0 |
| 1200 | 4 | 4 | 1.0 |
| 2270 | 4 | 3 | 1.0 |
| 1750 | 4 | 3 | 1.0 |
| 1351 | 3 | 3 | 1.0 |
| 1745 | 3 | 3 | 1.0 |
| 1620 | 3 | 3 | 1.0 |
| 1550 | 3 | 3 | 1.0 |
| 1800 | 3 | 3 | 1.0 |
| 1450 | 3 | 3 | 1.0 |
| 1654 | 3 | 3 | 1.0 |
| 1590 | 3 | 3 | 1.0 |
| 1510 | 3 | 2 | 1.0 |
| 1690 | 3 | 2 | 1.0 |
| 3600 | 3 | 2 | 1.0 |
| 1000 | 3 | 2 | 1.0 |
| 836 | 3 | 2 | 1.0 |
| 1710 | 3 | 2 | 1.0 |
| 1260 | 3 | 2 | 1.0 |
Menunjukkan 30 puncak terbaik disokong daripada 412 jumlah untuk N-O bond.
Logik spektrum
Tugasan kumpulan berfungsi menjadi lebih yakin apabila beberapa jalur yang dijangkakan muncul bersama. Gunakan halaman ini untuk mencari puncak yang paling disokong, kemudian sahkan bahawa sampel yang sama menunjukkan corak yang koheren dan bukannya satu hit terpencil.
Penggunaan dunia sebenar
Halaman-halaman ini berguna untuk analisis bahan yang tidak diketahui, penjelasan puncak dalam laporan, penyelesaian masalah polimer, dan mengesahkan sama ada keluarga bahan calon adalah boleh dipercayai secara kimia.
Kesilapan biasa
- Menggunakan satu halaman kumpulan berfungsi sebagai keputusan bahan lengkap tanpa memeriksa spektrum yang lain.
- Dengan menganggap jalur yang paling kuat sentiasa menjadi yang paling diagnostik.
- Melupakan bahawa pemprosesan, bahan tambahan, penuaan, dan campuran boleh mengalihkan atau melebarkan puncak yang dijangkakan.
Nasihat pengesahan
Gunakan DSC, GC-MS, atau TGA apabila beberapa keluarga bahan berkongsi jalur yang serupa atau apabila kesan campuran menyebabkan tugasan FTIR tidak pasti.
Literatur di sebalik penetapan ini
-
1000 cm⁻¹ keyakinan 1.0
“The peaks observed in IR at bending peak observed at in IR and no peaks observed in 1000cm(cid:2)1 1106 and 961 and in Raman at 1103 and”
Arjunan 等 - 2012 - Quantum chemical studies and vibrational analysis DOI: 10.1016/j.saa.2012.08.053 -
1170 cm⁻¹ keyakinan 1.0
“film 1170cm-1 1180cm-1 same from to suggesting possible transformation from to This showed no film apparent defect on its surface.”
Arshad 等 - 2019 - Dielectric and Structural Properties of Poly(vinyl DOI: 10.1155/2019/5961563 -
1302 cm⁻¹ keyakinan 1.0
“cm-1 cm-1, characteristic peaks at 1302 and 1416 which correspond to vibrational modes 3-) (COO-) of nitrate (NO and acetate ions [50,51].”
Sol-Gel Synthesized High Entropy Metal Oxides as High-Performance Catalysts for Electrochemical Water Oxidation DOI: 10.3390/molecules27185951 -
3326 cm⁻¹ keyakinan 1.0
“carbon-hydrogen or C-O band stretching (1233 this is why no characteristic peak was appeared due to cm-1 The broad peak at 3326 is the characteristic band for”
Awal 等 - 2012 - Thermal analysis and spectroscopic studies of elec DOI: 10.1007/s10973-011-1875-0 -
405 cm⁻¹ keyakinan 1.0
“This N-O bond is also proved by XPS on deconvolution peaks detected at 404.8 and 531.5 eV in N 1s and O 1s, respectively.”
Azami 等 - 2017 - Formation of predominant interstitial N-TiO2 using DOI: 10.5004/dwt.2017.21496 -
2917 cm⁻¹ keyakinan 1.0
“cm-1 Aand Bsites IR-spectrum of BaM sample shows the band around 2917 and 3416 assign O-H cm-1, CO2stretching of water, the N-O elongating at about 1481-1484 vibration of anti-symmetrical at α-Fe cm-1, cm-1, 1642 and 2O stretching metal-O a”
Effect of rare earth and transition metal La-Mn substitution on electrical properties of co-precipitated M-type Ba-ferrites nanoparticles DOI: 10.1016/j.jre.2018.08.005 -
1413 cm⁻¹ keyakinan 1.0
“The absorption bands 1413 cm-1 3-, cm-1 cm-1 at 815.25 and 728.12 were assigned to the N-O bending vibration of NO and to C-N at 815.25 cm-1 and 728.12 cm-1 were assigned to the N-O bending vibration of NO3-, and to C-N stretching from the”
Effect of Ratio in Ammonium Nitrate on the Structural, Microstructural, Magnetic, and AC Conductivity Properties of BaFe12O19 DOI: 10.3390/ma11112190 -
1636 cm⁻¹ keyakinan 1.0
“lysation reaction of to cm(cid:1)1 C¼¼C The sharp peak at 1636 indicates the bond of the synthesized difunctional monomer and no unreacted materials like 3-MPTS and acrylic acid.”
Synthesis of UV-curable difunctional silane monomer based on 3-methacryloxy propyl trimethoxysilane (3-MPTS) and its UV-curing characteristics and thermal stability DOI: 10.1002/app.31266