What absorbs at 683 cm⁻¹ in an FTIR spectrum?
683 cm⁻¹ yakınındaki bir bant birkaç fonksiyonel gruba işaret edebilir. Aşağıda, her birini ne kadar yayınlanmış kanıtın desteklediğine göre sıralanmış en olası atamalar bulunmaktadır — her biri literatüre (DOI) kadar izlenebilir ve 130.000＇den fazla referans spektrumumuz ve bilgi grafiğimizle çapraz doğrulanmıştır.
Backed by 6 cited sources
Hızlı cevap
A band near 683 cm⁻¹ is usually interpreted by checking which functional groups repeatedly co-occur there in the literature, then confirming at least one or two additional peaks in the same sample. This page ranks those assignments by accumulated evidence rather than by a single fixed textbook rule.
Olası fonksiyonel grup atamaları
| Fonksiyonel grup | Destekleyici gerçekler | Atıf yapılan kaynaklar | En yüksek güven |
|---|---|---|---|
| Ring structure | 1 | 1 | 1,0 |
| C c single bond | 1 | 1 | 1,0 |
| Carbonate | 1 | 1 | 1,0 |
| Metal oxygen | 1 | 1 | 1,0 |
| Phosphate (PO4) | 1 | 1 | 1,0 |
| N h | 1 | 0 | 1,0 |
Sıralama, tek bir otoriter kural değil, birikmiş literatür kanıtını yansıtır. Her zaman numune bağlamınıza göre onaylayın.
Spektrum mantığı
This band becomes meaningful only when read with its neighboring peaks. In practice, analysts first look at the assignments above, then check whether the same sample also shows other peaks expected for the same structural motif. A lone band near 683 cm⁻¹ is usually not enough for material identification by itself.
Gerçek dünya kullanımı
Bu tür sorgu, polimer tanımlama, bilinmeyen plastik taraması, kalite kontrol sorun giderme, geri dönüştürülmüş malzeme doğrulama ve literatür destekli pik atama incelemesinde yaygındır.
Sık yapılan hatalar
- En az bir veya iki destekleyici piki kontrol etmeden tek bir izole bandı bir malzemenin kanıtı olarak kabul etmek.
- Örtüşme göz ardı ediliyor: birden çok fonksiyonel grup aynı dalga sayısına yakın katkıda bulunabilir.
- Katkı maddeleri, karışımlar, oksidasyon veya kontaminasyon spektrumu bozabileceğinde doğrulamayı atlamak.
Doğrulama tavsiyesi
Belirsizlik devam ettiğinde, özellikle karışımlar, bozunmuş numuneler ve doldurulmuş polimerler için hipotezi DSC, GC-MS veya TGA ile doğrulayın.
Bu atamaların arkasındaki literatür
-
Phosphate (PO4) güven 1,0
“The third intense band at 683 is assigned to the symmetric stretching of P-O-P Q2 Q1 cm-1 linkages in and structural unit [50].”
El-Hezzat 等 - 2021 - Structure - Properties study of Na2O-CaO-PbO-P2O5 DOI: 10.1016/j.solidstatesciences.2021.106666 -
güven 1,0
“The highest-frequency A1g mode at 683 cm-1 is assigned to the symmetric stretching vibrations of the oxygen atoms with respect to the metal ion Coatings2023,13,1250 8of15 in the tetrahedral sites, a mode that can be also described as tetrah”
Synthesis of CoFe2O4 through Wet Ferritization Method Using an Aqueous Extract of Eucalyptus Leaves DOI: 10.3390/coatings13071250 -
Metal oxygen güven 1,0
“cm-1 at ~615 shows the single degenerate symmetric vibrations of O-Cu-O linkages along with vibrations units.(73,76) in TeO After the annealing treatment, the 4 cm-1 sharp peak at 683 which corresponds to TeO 4”
Kaur 等 - 2020 - Structure of copper tellurite and borotellurite gl DOI: 10.13036/17533562.61.1.007 -
Carbonate güven 1,0
“tion band at 683 was associated with carbonate”
Identification of pigments used in a Qajar manuscript from Iran by using atomic and molecular spectroscopy and technical photography methods DOI: 10.1186/s40494-022-00665-x -
C c single bond güven 1,0
“The band appearing at 683 ± 2 1612 ± 1 cm-1 was assigned the C-C macrocycle ring deformation.”
Optical Absorption and Visible Photoluminescence from Thin Films of Silicon Phthalocyanine Derivatives DOI: 10.3390/ma7096585 -
güven 0,9
“Explicit assignment: 'two bonds representing the α-phase of PA12 were observed at wavenumber of 576 and 683'”
Surface modification of the laser sintering standard powder polyamide 12 by plasma treatments DOI: 10.1002/ppap.201800032